The most prominent feature of this product is: a strong rust spots role of greatly reducing the anti-rust rate after the phosphate treatment to solve the problems of the pre-treatment manufacturers over the years: the workpiece in the easy anti-phosphate treatment rust. 

 Role: 

 ◆ phosphate coating crystalline dense, fine 
 ◆ shorten the time of film into 
 ◆ reduce the consumption of pharmaceutical 
 ◆ improve Coating corrosion resistance 

 Where applicable: 

 ◆ into zinc and zinc alloy coating. 
 Co the Jin Jingqiang alkaline degreasing ◆ steel, zinc and zinc 
 ◆ the treatment of iron and steel parts pickled. 

 Features: 

 ◆ has a strong anti-rust spots. Workpiece back to the rust rate can be greatly reduced, to solve the problems of pre-treatment manufacturers over the years: the workpiece after phosphating easy to return to rust. 
 ◆ activity of ultra-high. Table transfers the active role of the general plastic titanium sheet swap several times, 2-4 minutes of the general table transfers, table transfers simply, iron and steel: about 5 seconds, zinc and zinc alloys: 1 seconds or so, can greatly shorten the phosphating time and lower phosphide temperature. 
 ◆ to improve the quality of the phosphate film to eliminate the defect of alkaline degreasing or pickling rust corrosion caused by unequal, increasing the number of nuclei density and corrosion resistance of phosphate coatings improve the appearance of the phosphate film. 
 ◆ not choose water quality. Table transfers containing water softener, so when the preparation is not picky about water quality, the ratio of the concentration of 0.05% -0.2%. 
 ◆ long life. Table swap containing stabilizer, so the activity of slow decay, long life, usually 1 kilogram table swap deal with an area of ??2000 square meters of the workpiece can be compared with the general table transfers, overall costs can be reduced by 1.5-2 times. 

 Process parameters: 

 ◆ Use the concentration of 0.1-0.2% 
 ◆ PH value :8-9 
 ◆ Temperature: room temperature 
 ◆ Time: steel: more than 5 seconds; zinc and zinc alloys: more than 1 second. 

 How to use: 

 ◆ slotted: The dose of good plastic titanium surface modifier is soluble in water, stirring constantly, let it dissolve completely, you can use. 
 ◆ Bath maintenance: PH value of the timed test bath, and add the right amount of glue titanium surface modifier, so that the bath pH value in the 8-9 
 (Typically covering an area of ??1000m, the need of additional the 0.5Kg glue titanium surface adjusting agent). If the acid to enter the bath often can 
 And powder to help adjust the PH value between 8-9. 
 ◆ slot change: When the bath use for some time, if the bath began to change color, on film to slow down, the film uneven table adjust the effect of 
 Good phenomenon, this time should be considered to replace the bath. 

 Note: 
 ◆ Table adjust tank water to go ionized water is best, try to avoid the use of calcium and magnesium content of hard water to prevent the bath aging 
 Accelerated. 
 ◆ Table adjust the workpiece without washing, the best exposure to the air more than 1 minutes to ensure that the table tone effect. 
 ◆ mixing and vibration bath table tone effect